Supply of Plastic Refractory and Super Castable Refractory
2023_RVUNL_823170_1
N-PAR/B/MMC1/PD01/6000002757
Open Tender
Miscellaneous
Fixed-rate
30 days
PTPP PARICHHA JHANSI
AS PER TSD
2 documents required · 2 mandatory
₹1,180
DY GM(ACCOUNT)/DY CAO
₹15,000
30 Aug 2023
21 Jul 2023
17 Aug 2023
21 Jul 2023
16 Aug 2023
21 Jul 2023
21 Jul 2023 - 16 Aug 2023
REFRACTORY SUPERCASTABLE ALUMINA 68-72%, Super Castable Refractory As per Following Specification:Al2O3:68-72%, CaO:5.2-6%, Fe2O3:4.8-5.5%, Max Service Temp:1450 °C, Max Grain Size:5mm, Water required for casting:10-11%, Dry Density:2.50-2.65 g/cc, (After drying at 110 °C/24 Hrs), CCS:350-450 Kg/Cm2( after drying at 110 °C/24 Hrs) Refractoriness, Orton/°C PLC, % (After Heating at 1100 deg C/3Hrs: -0.30 to +0.30) After heating at 1400 deg C/3 Hrs: -1.60 to +1.70)
REFRACTORY PLASTIC ALUMINA 82.5-85.5, Plastic refractory As per Following Specification:Al2O3:82.5-85.5%, Fe2O3:0.50-0.85, Max Service Temp:1700 °C, Max Grain Size:3mm, PRE-8 Liquid for ramming:9.7-10.7%, Dry Density :2.70-2.85 g/cc, (After drying at 110 °C/24 Hrs), CCS:260-430 Kg/Cm2( after drying at 110 °C/24 Hrs) Refractoriness, Orton/°C PLC, % (After Heating at 550 °C/3Hrs: -0.3 to +0.3) After heating at 815 °C/3 Hrs: -0.3 to +0.3)
REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND #CASTABLE INSULATION)
REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND –CASTABLE INSULATION)
REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND –CASTABLE INSULATION) (Specification (Al2O3:82.5-85.5%,Fe2O3:0.50-0.85, Max Service Temp:1700oC, Max grain size:3mm, PRE-8 Liquid for ramming:9.7-10.7%, Dry density:2.70-2.85g/cc(After drying at 110oC/24Hrs), CCS:260- 430Kg/Cm2 (after dryingat 110oC/24Hrs),Refractoriness, Orton/oC PLC, %(After Heating at 550oC/3Hrs: -0.3 to +0.3; After Heating at 815oC/3Hrs: -0.3 to +0.3
REFRACTORY PLASTIC ALUMINA 82.5-85.5, PLASTIC REFRACTORY AS PER FOLLOWING SPECIFICATION:AL2O3:82.5-85.5%, FE2O3:0.50-0.85, MAX SERVICE TEMP:1700 °C, MAX GRAIN SIZE:3MM, PRE-8 LIQUID FOR RAMMING:9.7-10.7%, DRY DENSITY :2.70-2.85 G/CC, (AFTER DRYING AT 110 °C/24 HRS), CCS:260-430 KG/CM2( AFTER DRYING AT 110 °C/24 HRS) REFRACTORINESS, ORTON/°C PLC, % (AFTER HEATING AT 550 °C/3HRS: -0.3 TO +0.3) AFTER HEATING AT 815 °C/3 HRS: -0.3 TO +0.3) After Heating at 1400oC/3Hrs: -1.60 to +1.70)
REFRACTORY SUPERCASTABLE ALUMINA 68-72%, FIRE CRETE SUPER CASTABLE REFRACTORY ( TYPE -70% AL CASTABLE, NATURE OF BOND –CASTABLE INSULATION)
FIRE CRETE REFECTORY, FIRE CRETE REFECTORY - As per Following Specification:Al2O3:68-72%, CaO:5.2-6%, Fe2O3:4.8-5.5%, Max Service Temp:1450 °C, Max Grain Size:5mm, Water required for casting:10-11%, Dry Density:2.50-2.65 g/cc, (After drying at 110 °C/24 Hrs), CCS:350-450 Kg/Cm2( after drying at 110 °C/24 Hrs) Refractoriness, Orton/°C PLC, % (After Heating at 1100 deg C/3Hrs: -0.30 to +0.30) After heating at 1400 deg C/3 Hrs: -1.60 to +1.70)
GUPTA REFRACTORIES
tech_eval.pdf
boq_comp_chart.xlsx
xlsx
Download all tender documents and submit your bid
Disclaimer: TenderKart has made every reasonable effort to ensure that the information on this page is accurate and authentic, however it cannot be held liable for any third-party claims or losses or any damages. TenderKart makes no warranty, expressed or implied, as to the results obtained from the use of this information. If you notice any error or omission, please let us know at .