Nagercoil Corporation Providing Speed Breaker at Various Roads joining at Highways Road in Corpoartion areas

Providing and laying bituminous concrete to 30mm thick using 0.13 cum of 19.00-9.50mm graded metal,0.17 cum of 9.50-2.36 mm graded metal and 0.26 cum of 2.36mm & below metal by adding the shredded plastic waste over the aggregate heated to 170 degree celcious in the central hot mix plant,mixed well with 45.27Kgs hot bitumen VG 30 Bitumen (160 degree celcious) 60/70 grade for premixing per 10sqm to lay 30mm compacted thick of bituminious concrete including the cost of materials (the cost of municipality/ Corporation Plastic Waste obtained by the contractor from the Municipality/ Corporation will be Recovered) and conveyance of all materials to CMP site, heating the bitumen and aggregates to the required temperature and mixing the minimum required Temperature in central hot mix plant 20-30 tonnes capacity conveying the mix by tipper trucks to paver site,spreading the mix in required temperature for uniform thickness of 30mm with mechanical paver to the specified grades and cross sections and consolidated by 80-100 KN Vibratory Roller/ Pneumatic roller to the required density etc. including labour for loading bitumen in to bitumen tank and metal to feeder unit labour for attending to paver site etc. including hire charges and fuel charges for 20-30t CMP with bitumen boiler,tipper trucks, Paver finisher/9m Paver finisher,Vibratory/Pneumatic rillers and all other tools and plantsrequired, including all other incidental charges etc. complete as per specification using CMP clauses 507 of MORTH REV-5 specifications.

Providing and laying of hot applied Thermoplastic compound 2.5 mm thick including reflectorising glass beads @ 250 gms per sqm area, thickness of 2.5 mm is exclusive of surface applied glass beads as per IRC:35- 2015. The finished surface to be level, uniform and free from streaks and holes etc., complete as per MoRT&H specification No.803

Providing and fixing reflective road studs of ‘category A’ Raised pavement markers made out of poly carbonate / methyl methercrylate/ABS moulded body confirming to ASTM D 788 and reflective panels with micro prismatic lens capable of providing total internal reflection of the light entering the lens face with retro reflectance and chromaticity values conforming to ASTM D4280. The reflective raised pavement markers shall also confirm to the MoRT&H circular No RW / NH. 33023/10/ 97-DO. III dt 11.06.97. The height, width and length shall not be less than 15 mm, 90 mm and 100 mm and with minimum reflective area of 13 Sq.cm on each side and the slope to the base shall be 35 (+/-) 5 degree. Each reflector shall have a CIL not less than values specified in Table 2 of said MoRT&H circular. The strength of detachment of the integrated cylindrical shanks, (of diameter not less than 19 (+/-) 2mm and height not less than 30 (+/-) 2 mm) from the body is to be a minimum value of 500 Kgf. Fixing will be by drilling holes on the road for the shanks to go inside, without nails and using epoxy resin based adhesive as per manufacturer’s recommendation and complete as directed by the Engineer. The marker shall support a load of 13635 Kg tested in accordance with ASTM D4280 and confirming to IRC 35 - 2015 guidelines and MoRT&H specification 804 etc., complete