Repair of Central workshop

Demolishing cement concrete manually/ by mechanical means including disposal of material within 50 metres lead as per direction of Engineer - in - charge. Nominal concrete 1:3:6 or richer mix (i/c equivalent design mix)

Providing, mixing and applying SBR polymer (of approved make) modified Cement mortar in proportion of 1:4 (1 cement: 4 graded coarse sand with polymer minimum 2% by wt. of cement used) as per specifications and directions of Engineer-in-charge. Note: Measurement and payment: The pre-measurement of thickness shall be done just after the surface preparation is completed and Payment under this item shall be made only after proper wet curing has been done and surface has been satisfactorily evaluated by sounding / tapping with a blunt metal instrument and/or the 75mm size cube crushing strength at the end of 28 days to be not less than 30 N/Sqmm2). 25 mm average thickness in 2 layers

Demolishing brick work manually/ by mechanical means including stacking of serviceable material and disposal of unserviceable material within 50 metres lead as per direction of Engineer-in-charge. In cement mortar

Providing and applying of MAPEI MAPELASTIC SMART two-component, high flexible, elastic cementitious mortar made from synthetic fibres, special admixtures and synthetic polymers in water dispersion with an elongation of 120% (DIN 53504), Static crack bridging ability of >2.5mm (EN 1062-7), Permeability to water vapour sD = 3.6 m, µ = 1800 (EN ISO 7783-1), Impermeability to water < 0.05 kg/m²·h0.5 (EN 1062-3), Permeability to CO₂ sDCO2 >50m (EN 1062-6), Reaction to fire (Euroclass): E (EN 13501-1), adhesion to concrete after 28 days: 1.3 N/mm² (EN 1542) when applied @ 2mm thickness on the surface prepared for waterproofing to be carried out to ensure the mechanical properties of the product. Apply two layers of the product, with a non-woven polypropylene fabric of MAPETEX SEL 150 gsm with a weight of 150 g/m², placed between the first and second layers with a min overlap of 5 cm. The application of the product shall be carried out after the thorough preparation of the surface which includes cleaning, crack treatment, grouting. Minimum of 10mm all round gap to be provided between the pipe and the core. Provide shuttering below the core and providing and applying the hydro-swellable paste for joint treatment. MAPEPROOF SWELL Single component hydro-expensive paste. Providing and applying of super flow micro-concrete with dual shrinkage-compensation called MAPEFILL 06, high flow, single component formulation. The micro-concrete shall be in accordance to EN 1504-6 & shall exhibit a compressive strength minimum of >40 MPa at 7 days and >55 MPa at 28 days, a flexural strength of >9 Mpa after 28 days, adhesion to concrete substrate of >2.5 Mpa after 28 days. The microconcrete shall not require polymer bonding agent as primer. Can be used for grouting of gaps with thicknesses ranging from 50 mm to 250 mm and shall have fresh wet density in excess of 2250 kg/M3.

Providing and applying of MAPEI MAPELASTIC SMART two-component, high flexible, elastic cementitious mortar made from synthetic fibres, special admixtures and synthetic polymers in water dispersion with an elongation of 120% (DIN 53504), Static crack bridging ability of >2.5mm (EN 1062-7), Permeability to water vapour sD = 3.6 m, µ = 1800 (EN ISO 7783-1), Impermeability to water < 0.05 kg/m²·h0.5 (EN 1062-3), Permeability to CO₂ sDCO2 >50m (EN 1062-6), Reaction to fire (Euroclass): E (EN 13501-1), adhesion to concrete after 28 days: 1.3 N/mm² (EN 1542) when applied @ 2mm thickness on the surface prepared for waterproofing to be carried out to ensure the mechanical properties of the product. Apply two layers of the product, with a non-woven polypropylene fabric of MAPETEX SEL 150 gsm with a weight of 150 g/m², placed between the first and second layers with a min overlap of 5 cm. The application of the product shall be carried out after the thorough preparation of the surface which includes cleaning, crack treatment, grouting. MAPEFLEX PU45 will be used to fill the gap between the brick and RCC.

Providing, mixing and applying SBR polymer (of approved make) modified Cement mortar in proportion of 1:4 (1 cement: 4 graded coarse sand with polymer minimum 2% by wt. of cement used) as per specifications and directions of Engineer-in-charge. Note: Measurement and payment: The pre-measurement of thickness shall be done just after the surface preparation is completed and Payment under this item shall be made only after proper wet curing has been done and surface has been satisfactorily evaluated by sounding / tapping with a blunt metal instrument and/or the 75mm size cube crushing strength at the end of 28 days to be not less than 30 N/Sqmm2). 12 mm average thickness.

Providing and laying APP (Atactic Polypropylene Polymer) modified prefabricated five layer, 3mm thick water proofing membrane, black finished reinforced with glass fibre matt consisting of a coat of bitumen primer for bitumen membrane @ 0.40 litre/sqm by the same membrane manufactured of density at 25°C, 0.87 - 0.89 kg/litre and viscocity 70 - 160 cps. Over the primer coat the layer of membrane shall be laid using butane torch and sealing all joints etc., and preparing the surface complete. The vital physical and chemical parameters of the membrane shall be as under : Joint strength in longitudinal and transverse direction at 23°C as 350/300 N/5 cm. Tear strength in longitudinal and transverse direction as 60/80N. Softening point of membrane not less than 150°C. Cold flexibility shall be upto -2°C when tested in accordance with ASTM, D - 5147. The laying of membrane shall be got done through the authorised applicator of the manufacturer of membrane : 3 mm thick

Providing and applying white cement based putty of average thickness 1 mm, of approved brand and manufacturer, over the plastered wall surface/wall partition to prepare the surface even and smooth complete.

Wall painting with premium acrylic emulsion paint of interior grade, having VOC (Volatile Organic Compound ) content less than 50 grams/ litre of approved brand and manufacture, including applying additional coats wherever required to achieve even shade and colour. Two coats

Applying priming coats with primer of approved brand and manufacture, having low VOC (Volatile Organic Compound ) content. With water thinnable cement primer on wall surface having VOC content less than 50 grams/ litre