Rate contract of reputed firms or manufacturers for lining of on farm water reservoirs with use of HDPE plastic films or Polyethylene films or HDPE Geo membrane at the farmers fields under Horticulture Development Schemes during 2021-22

HDPE Sheet (BIS 10889/2004):± 300 micron Thickness of HDPE film Tolerance on thickness % +/- ± 20 Density at 27˚C, Kg/M3 940-952.4 Melt flow index Gm/ 10 minute - 0.20- 0.80 % Carbon black content by mass - 2.50 ± 0.5 Tensile strength at break kg/cm2 - Min, MD-300, Min, TD- 250 % elongation at break- Min, MD- 300, Min, TD-300 Visual appearance- Film shall be uniform in color, texture & finish. The material shall be free from pinholes and reasonably free from undispersed raw materials, streaks & particles of foreign matter

HDPE Sheet (BIS 10889/2004):± 500 micron Tolerance on thickness % +/- -± 20 Density at 27˚C, Kg/M3 - 940-952.4 Melt flow index Gm/ 10 minute - 0.20- 0.80 % Carbon black content by mass - 2.50 ± 0.5 Tensile strength at break kg/cm2 - Min, MD-300, Min, TD- 250 % elongation at break - Min, MD- 300, Min, TD-300 Visual appearance - Film shall be uniform in color, texture & finish. The material shall be free from pinholes and reasonably free from undispersed raw materials, streaks & particles of foreign matter

Polyethylene Films and sheet (BIS 2508/2016) 0.3 mm Thickness, mm, Min- (0.3mm) Tolerance on thickness % +/- - ± 10 Tensile properties, Min Average Yield strengh, N/mm2 Break strengh, - Min, MD- 280kg/cm2, Min, TD-230kg/cm2 Yield elongation, Min percent Break elongation, percent - Min, MD- 800, Min, TD-900 Tear resistance, Min average- Min, MD- 3800 g, Min, TD-3900 g Melt flow index g/ 10 minute - 0.10 to 2.0g /10 min. Density at 27˚C - 0.913 to 0.928 g/ml Puncture resistance, Min average, N Ash content % - < 2.0 Visual appearance - Film shall be uniform in color, texture & finish. The material shall be free from pinholes and r free from dispersed raw materials, streaks & particles of foreign matter

Polyethylene Films and sheet (BIS 2508/2016) 0.5 mm Thickness, mm, Min (0.5mm) Tolerance on thickness % +/- ± 10 Tensile properties, Min Average Yield strengh, N/mm2 - 7 Break strengh, - 13 N/mm2 Yield elongation, Min percent- 12 Break elongation, percent - 700 Tear resistance, Min average - 62 Min average, N Melt flow index g/ 10 minute - 0.10 to 1.0g /10 min. Density at 27˚C - >0.930g/ml Puncture resistance, Min average, N - 160 Ash content % - < 2.0 Visual appearance - Film shall be uniform in color, texture & finish. The material shall be free from pinholes and free from dispersed raw materials, streaks & particles of foreign matter

HDPE Geo-membrane (BIS 15351/2015) 0.3 mm Thickness, mm, Min 0.25 mm Mass, g/m2, Min - 250 Dimensions (length & width) - As declared +1% with no negative tolerance % Carbon black content, Min - 2.5 ± 0.5 Breaking load on 20cm X 10 cm strip, N, Min before UV exposure - 3300 Strain at maximum load, percent - 20 ± 5 Breaking load on 20cm X 10 cm strip, N, Min after UV exposure of 1000 h - 80% of actual original value Impact failure load, at 1524 mm drop, Min, gram force at 50 % failure - 1150 Tear resistance, N, Min - 100 Puncture resistance, N, Min - 300 Bursting strength (ball burst), N/cm2, Min - 60 Seam strength before UV exposure N/mm, Min - 15 Hydrostatic resistance - No leakage at 10 kg/cm2 Ash content - 1%

HDPE Geo-membrane (BIS 15351/2015) 0.50 mm Thickness, mm, Min - 0.50 mm Mass, g/m2, Min - 420 Dimensions (length & width) - As declared +1% with no negative tolerance % Carbon black content, Min - 2.5 ± 0.5 Breaking load on 20cm X 10 cm strip, N, Min before UV exposure - 6600 Strain at maximum load, percent - 20 ± 5 Breaking load on 20cm X 10 cm strip, N, Min after UV exposure of 1000 h - 80% of actual original value Impact failure load, at 1524 mm drop, Min, gram force at 50 % failure - 1840 Tear resistance, N, Min - 250 Puncture resistance, N, Min - 500 Bursting strength (ball burst), N/cm2, Min - 110 Seam strength before UV exposure N/mm, Min - 30 Hydrostatic resistance - No leakage at 15 kg/cm2 Ash content - 1%

HDPE Geo-membrane (BIS 16352/2015) Thickness, mm, Min - 0.50 mm Dimensions (length & width) - As declared ± 1% % Carbon black content, Min - 2.0 to 3.0 Breaking strength K N/m, Min - 14 Breaking elongation, Percent, Min, - 700 Seam strength K N/m, Min - 85% of the original actual fabric strength or unbreakable seam Retention of breaking strength after UV exposures of 500 h N, Min - 85% of the original actual fabric strength Tear resistance, N, Min - 63 Puncture resistance, N, Min - 160 Stress crack resistance h, Min - 300 Breaking elongation, Percent, Min, - 700 Hydrostatic resistance - No leakage at 15 kg/cm

International Packaging Products Pvt Ltd

Tara Tradelink Pvt Ltd

Shree Kushal Polymers

EMMBI INDUSTRIES LTD

RAJ POLYFABRICS PRIVATE LIMITED

GUJARAT CRAFT INDUSTRIES LIMITED

Kohinoor Proofing Industries

VIGHNAHAR PACKAGING PRODUCTS

HARIOM FLEXIPACK INDUSTIRES

AQUAVISION AGRO PVT LTD

ESSEN MULTIPACK .LTD

TEXEL INDUSTRIES LIMITED

DAISY INDUSTRIES

Rishi FIBC Solutions Private Limited

CLIMAX SYNTHETICS PVT. LTD.