TN-25141 Supply of various type of Adhesive to KSTPS, Kota

Instant Adhesive(20 gm pack), Ethyl cyanoacrylate based transparent colorless to straw colored instant adhesive , Viscosity ,Cone & plate(25° C, Shear Rate: 3000 s-1) is 12 to 22 cPs, Lap Shear Strenght (ISO 4587) on steel is 2250 psi, Tensile Strength (ISO 6922) on Buna-N is 1890 psi.(ICS CODE-1304000038)

Instant Adhesive (20 gm pack), Ethyl cyanoacrylate based transparent colorless to straw colored liquid, viscosity (Brookfield LVF, 25° C Spindle 1, speed 30 rpm) is 25 to 55 cP, Vapor Pressure is upto 1 hPa, SofteningPoint(DIN EN 1427) is 165° C, Lap Shear Strength (ISO 4587) is 3770 psi, Tensile Strength (ISO 6922) is 3625 psi, Shear Strength (ISO 4587) is 160 psi

Instant adhesive (20 gm Pack)- Ethyl cyanoacrylate based Clear colorless slightly hazy to light yellow instant adhesive, Viscosity ( Cone & Plate, 25 °C,PHYSICA MK22 @ 100 s-1) is 900 to 1500 cP, Dielectric Breakdown Strength (IEC 60243-1) is 25 kV/mm, Lap Shear Strength (ISO 4587)Steel (grit blasted) 2350 psi.

Thread Locker (50 ml pack)- Dimethacrylate ester based blue color anaerobic threadlocker, Viscosity (Cone & Plate, 25 °C Cone 35/2°Ti @ shear rate 129 s-1) is 350 cP, Compressive Shear Strength (ISO 10123) on Steel pins and collars is 1100 psi, Breakloose Torque, ISO 10964 (Pre-torqued to 5 N·m) is 24 N.M., This product has been tested to -75°C (-100 F).

Thread Locker (250 ml)- Dimethacrylate ester based green color anaerobic threadlocker, Breakaway Torque ( ISO 10964) M10 steel nuts and bolts is 10 N.M, Compressive Shear Strength (ISO 10123) on Steel pins and collars is 780 psi, Viscosity (Brookfield - RVT, 25 °C, Spindle 1, speed 50 rpm) is 20 to 55 cPS.

Gasketing Compound (50 ml) - Dimethacrylate ester based orange color anaerobic flange sealant, Viscosity (Brookfield RVT, 25 °C Spindle 6, speed 20 rpm) is 23,000 to 35,000 cPS, Compressive Shear Strength (ISO 10123) on Steel pins and collars is 870 psi, Tensile Strength (ISO 6922) is 725 psi, Coefficient of Thermal Expansion (ISO 11359-2) 80×10-6 K-1.

Gasketing Compound (250 ml) - Dimethacrylate ester based orange color anaerobic flange sealant, Viscosity (Brookfield RVT, 25 °C Spindle 6, speed 20 rpm) is 23,000 to 35,000 cPS, Compressive Shear Strength (ISO 10123) on Steel pins and collars is 870 psi, Tensile Strength (ISO 6922) is 725 psi, Coefficient of Thermal Expansion (ISO 11359-2) 80×10-6 K-1.

Fast set Steel Putty 500 gm kit- Max Cure time is 12 minutes, Compressive Strength( ASTM D695) is 74.5N/mm2, Shear Strength (ASTM D1002).125mm gap, acid etched aluminium is 13.8 N/mm2 , Tensile Strength(ASTM D638) is 31.7 N/mm2 ,Hardness (ASTM D-2240) is 80 Shore D

Steel Putty 1 Lbs Kit - Metallic Grey color self levelling liquid for repairs and casting, Temperature range is –30° to +105°C, Working Life 25 minutes, Cure Time is 6 hours, Compressive Strength (ASTM D695) is 93.1 N/mm2, Shear Strength (ASTM D1002) .125 mm gap, acid etched aluminium is 13.1 N/mm2, Hardness (ASTM D-2240) is 86 Shore D

Metal Rebuilding -FixmasterSuperior Metal (1Kg. Pack)- Grey color epoxy, Working life is 20 min, Tensile Strength (ISO 527-2) is 3900 psi, Compressive Strength, @65ºC (ISO 604) is 19,490 psi, Lap Shear Strength (ISO 4587) on grit blasted MS is 2820 psi, Volume Shrinkage (ISO 1675) is 5%.