CECRI01102024MMP035201 W9 (WP4)7 - HEAT RESISTENCE PAINT TESTS AT NABL ACCREDITED LABORATORY

Amount

List of Tests

Odor Test - as per standerd ASTM D1296

Volatile organic compounds VOC content - as per standerd ASTM D2369- IS 101 Part 8-sec 2

Pot life and Viscosity of HRP mixture - as per standerd BS EN ISO 2431 or ASTM D 1200 or IS101 Part 1 Sec 5

Drying time - as per standerd ASTM D1640 or IS 101 Part 3, Sec 1

Density - as per standerd ASTMD1475 or IS 101 Part 1, Sec 7

Specular gloss - as per standerd BS 2782-5 520A or IS- 101-PART-4-SEC-4

Dry film thickness - as per standerd ASTM E376 or ASTM B499

Bend- Flexibility test room Temperature - as per standerd ASTM B571 or IS 101 Part 5 Sec 2

Bend- Flexibility test Low Temperature - as per standerd IS 101 Part 5 Sec 2 for reference

Adhesion cross hatch - as per standerd ASTM D 3359 Test Method A-B or BS3900-Part E6, 1 mm spacing

Adhesion Dolly test - as per standerd ASTM D4541

Hardness Scratch test - as per standerd ASTM D3363 - IS 101 Part 5 Sec 1

Water Resistance - as per standerd ASTM D870 for 168 Hrs

Fuel Resistance (ATF K-50) - as per standerd ASTM D 6943

Gearbox oil Resistance (OEP-70) - as per standerd ASTM D 6943

Hydraulic Oil (H-515) - as per standerd ASTM D 6943 for 168 h at 40 C

Grease Resistance (G382, G366, G355) - as per standerd ASTM D 6943 for 168 h at 40 C

Weather resistance - as per standerd ASTM G155 Duration 500 h Chamber condition: Temp: 42 ±3 °C

High Temperature Test - as per standerd MIL-STD-810G Method 501-5 for 24 hour Temperature up to 200 °C

Low temperature - as per standerd Test MIL-STD-810G Method 502-5 Procedure-II 4 h

Salt Spray - as per standerd MIL-STD-810 G Method 509-5 for 96 h

Combined Altitude Temperature and Humidity test CATH - as per standerd MIL-STD-810G (cycles: 10 cycles) (1 cycle=16 h)

Resistance to dust - as per standerd MIL-STD-810G Method 510-5 JSS 55555 Test No 14

Resistance to rain driving rain - as per standerd MIL- STD-810G Method 506-5- JSS 55555

Vibration Test - as per standerd MIL-STD-810G Method 514-6 (Main rotor frequency: 5.88Hz f=5.88Hz, A 1=0.144g f1 =17.65Hz, A2=1.765g)

Thermal shock - as per standerd MIL-STD-810G Method 503-5 Procedure I-B

Humidity resistance - as per standerd MIL-STD-810G, Method 507-5

Icing-freezing rain - as per standerd MIL-STD-810G Method 521-3- JSS 55555